TAC System - Quartz Climax 2 100 SiO2

TAC SYSTEM QUARTZ CLIMAX 2 100 SIO2 KITDouble ~ quad coat system._x000D_ Numai pentru Uz Profesional!Necesita uscare cu Lampa IR!This is SiO2 technology pushed to its limits, incorporating close to 100 of quartz concentration, making it not only theoretically the purest coating in the market, but also in practice.The kit includes the common applicator block and suedes, the Climax 100 and the Top Coat 2.0 in 50ml’s._x000D_ Short wave IR lamp 65C @ 20min per coat.Produs de Curăţare si Intreţinere Auto!_x000D_ _x000D_ Acesta este un Produs Chimic!_x000D_ Este destinat numai pentru Uz Profesional!Nu lăsaţi la indemana copiilor!Acest produs poate irita ochii si pielea!Intotdeauna purtaţi mănusi de protecţie!Product Description:Quartz Climax is Tac System's Professional choice for long term durable protection, ultra high solids, and extreme gloss. Quartz Climax is a two stage coating, providing maximum protection via the base layer and optimal surface properties with the top coat. Quartz Climax is a 100 SiO2 glass inorganic coating exclusively for professional use only._x000D_ Quartz Climax creates a transparent hard glass-like layer on the surface which also reflects extreme glossiness. With a separate application of the hydrophobic property, Climax immensely boots up the water repelency of the surface and offering a high quality of self-cleaning effect which ensures the long lasting shininess. Quartz Climax is suitable for all types of automotive paints._x000D_ Product Benefits:_x000D_ Highest Gloss. Extreme Slickness. Outstanding UV & Chemical Resistance. Super high solids coating coating. Great self cleaning properties due to super hydrophobic surface properties.Warnings: Always wear respirator & gloves during application. Ensure application area is free of loose contamination._x000D_ Directions:_x000D_ (In a well lit, temperature controlledbelow 25°C, & contamination free environment)_x000D_ - Base Coat: Frequent changing of suede & micro fiber towels are required._x000D_ Recommended Application Area ~ 1/2 Hood Size area - then change micro fiber suede. After even application of base coat across the surface, immediately use new towel and remove the coating residue from the panel. _x000D_ Wait 1hr between application of base and top coat._x000D_ - Top Coat: Requires less applicators than base coat and is a little more time forgiving than the base coat. Recommended Application Area ~ 3 panels, then switch suede. Coating removal towels are changed at the same frequency of the micro fiber suede applicators. After even application of top coat across the surface, immediately use new towel and remove the coating from the panel._x000D_ Tips / Alternate Uses:_x000D_ High spots are visible for 20-30min. If high spots are found within an hour of wipe off, they can be reactivated and removed with the base coat or top coat (on a new micro fiber applicator) depending on which coating was applied last._x000D_ For Optimal Results: _x000D_ First thoroughly wash vehicle with Ultra Foam/ Mystic Bubble/ Mystic Water Repellent then remove all embedded iron deposits from vehicle paint pores and surfaces using Iron Zero/ Iron Zero Foam. Next, polish vehicle surfaces to the highest level. After polishing, use Oil Zero to remove all polish residues from surfaces to ensure optimal bonding and durability for the coating application._x000D_ Max Efficiency:_x000D_ 1.Apply Base Coat then cure with IR lamps at 50°C-60°C for 30 minutes._x000D_ 2.Apply Top Coat then also cure with IR lamp._x000D_ Post Application Instructions:_x000D_ - Wait 1hr before topper can be added._x000D_ - 24 hrs before any water exposure. Unless IR lamps used at 50°C-60°C for 30 minutes._x000D_ - Wait 7 days before first wash._x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_ _x000D_